ABSTRACT
This study evaluated the hardness and modulus of elasticity of the dentin bond interface using total-etch(Single Bond /SB) and self-etch (Clearfil SE Bond/CSEB) adhesives associated with Nd:YAG Laser irradiation through the unpolymerized adhesives. Material and Methods: The occlusal surfaces of 12 human third molars were ground until superficial dentin was exposed. A standardized circular cavity was performed on the occlusal surface. Specimens were sectioned in the mesio-distal direction, and the 24 hemi-crowns were divided into four groups: Group SB/Control - SB + polymerization; GroupSB/Laser - SB + Nd:YAG laser (174.16J/cm2/60s/noncontact)+ polymerization; Group CSEB/Control CSEB +polymerization; Group CSEB/Laser - CSEB + Nd:YAG laser(174.16J/cm2/cm2/60s/non-contact) + polymerization. Composite were placed in the cavities and polymerized. The specimens were immersed in distilled water and stored in an oven at 37ºC for 24h and then submitted to nanoindentation in a Nano Indenter® XP appliance. Results: The results were submitted to ANOVA, Tukeystest and Students-t test (p < 0.05). Conclusion: It was concluded that the application of the Nd:YAG laser inboth adhesive systems did not changed the hybrid layer hardness; however, it increases the modulus of elasticityin the hybrid layer for both adhesives tested and it may bepreserves the integrity of the adhesive interface and its durability. Clinical relevance: The application of Nd:YA Glaser prior to photopolymerization of adhesive systems can increase the modulus of elasticity in the hybrid layerand may contribute to stress distribution in the adhesive interface during the polymerization preserving the integrity of the adhesive interface and its durability...
este estudo avaliou a dureza e o módulo de elasticidade da interface adesiva a dentina usando adesivo convencional (Sinngle Bond /SB) e adesivo autocondicionante (Clearfil SE Bond/CSEB) associados com irradiação do Laser Nd:YAH sobre os adesivos não polimerizados. Material e Métodos: As superfícies oclusais de 12 terceiros molares humanos foram desgastadas ate exposição de dentina superficial plana. Cavidades circulares padronizadas foram realizadas na superficie oclusal. Os espécimes foram seccionados no sentido mesio-distal, e as 24 hemicoroas foram divididas em quatro grupos: Grupo SB/Controle - SB + fotopolimerização; Grupo SB/Laser- SB + Laser Nd:YAG (174,16J/cm2/60s/não-contato)+ fotopolimerização; Grupo CSEB/Controle CSEB +fotopolimerização; Grupo CSEB/Laser - CSEB + LaserNd:YAG (174.16J/cm2/cm2/60s/ não-contato) +fotopolimerização. Restaurações de resina composta foram realizadas nas cavidades e fotopolimerizadas. Os espécimes foram armazenados em água destilada a 37 ºC por 24 h e submetidas a nanoindentação no aparelho Nano Indenter® XP. Resultados: Os resultados foram submetidos ao ANOVA, seguidos dos testes de Tukey e T-Student (p < 0,05). Conclusão:Foi concluído que a aplicação do Laser de Nd:YAG nos adesivos não alterou a dureza da camada híbrida;entretanto, aumentou o módulo de elasticidade de ambos os adesivos testados e talvez preserve a integridade da interface adesiva e sua durabilidade...